矽橡膠
一般屬性
| Classification | For general purpose, FDA (21CFR177 2600), BR | JIS B2401 4-C | ||||||||
| Grade | KE-931-U | KE-941-U | KE-951-U | KE-961-U | KE-971-U | KE-981-U | KE-961T-U | KE-971T-U | KE-871C-U | |
| Appearance | Milky white translucent | Grayish white | Miky white translucent | Grayish white | ||||||
| Density 23℃ g/cm³ | 1.07 | 1.11 | 1.14 | 1.22 | 1.3 | 1.42 | 1.17 | 1.2 | 1.29 | |
| Williams plasticity (10 min after remix) | 160 | 190 | 240 | 280 | 330 | 420 | 280 | 340 | 260 | |
| Curing agent | Curing agent name | C-8 | C-8 | C-8 | C-8 | C-8 | C-8 | C-8A | C-8 | C-8 |
| Standard addition quantity*¹ | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 0.5 | 2.0 | 2.0 | |
| Linear shrinkage*² % | 4.0 | 3.9 | 3.9 | 3.4 | 3.0 | 2.7 | 3.6 | 3.4 | 2.9 | |
| Physical strength | Hardness Durometer A | 31 | 43 | 52 | 63 | 71 | 84 | 62 | 71 | 72 |
| Tensile strength MPa | 4.7 | 6.5 | 8.2 | 7.3 | 7.5 | 8.8 | 9.7 | 8.8 | 6.9 | |
| Elongation at break % | 480 | 370 | 330 | 320 | 220 | 100 | 310 | 260 | 190 | |
| Tear strength crescent piece kN/m | 15*³ | 15*³ | 23*³ | 20*³ | 20*³ | 8 | 25*³ | 25*³ | 9 | |
| Compression set 180℃ x 22 h | 15 | 11*4 | 11*4 | 11*4 | 9*4 | 12*4 | 11*4 | 11*4 | 10 | |
| Dielectric breakdown strength Normal state kV | — | 23 | 24 | 25 | 25 | 24 | 24 | 23 | — | |
| Volume resistivity Normal state TΩ．m | — | 7 | 8 | 6 | 3 | 4 | 4 | 4 | — | |
| Classification | Dynamic fatigue durability | Vibration control | For power connector | JIS B2401 4-C | |||||||
| Grade | KE-9551-U | KE-5151-U | KE-5550-U | KE-501EM-U | KE-7211-U | KE-7212-U | KE-7213-U | X-30-3893-U | KE-9590-U | ||
| Appearance | Milky white translucent | Pale yellow | Milky white translucent | Light gray | Gray | Blue-white | Black | Milky white translucent | |||
| Density 23℃ g/cm³ | 1.12 | 1.1 | 1.25 | 1.10 | 1.15 | 1.20 | 1.97 | 1.09 | 1.15 | ||
| Williams plasticity (10 min after remix) | 200 | 170 | 370 | 170 | 220 | 250 | 190 | 290 | 220 | ||
| Curing agent | Curing agent name | C-8A | C-8B | C-8 | C-15 | C-3 | C-3 | C-8 | C-8A | C-8 | |
| Standard addition quantity*¹ | 0.6 | 1.0 | 2.0 | 1.5 | 1.3 | 1.3 | 2.0 | 1.0 | 2.0 | ||
| Linear shrinkage*² % | 3.3 | 3.9 | 5.2 | 3.9 | — | — | — | — | 3.9 | ||
| Physical strength | Hardness Durometer A | 50 | 54 | 52 | 53 | 54 | 58 | 45 | 40 | 51 | |
| Tensile strength MPa | 6.6 | 7.7 | 9.3 | 7.7 | 11.0 | 9.2 | 2.5 | 7.4 | 8.8 | ||
| Elongation at break % | 310 | 450 | 730 | 520 | 780 | 680 | 320 | 680 | 400 | ||
| Tear strength crescent piece kN/m | 6 | 15 | 38 | 19 | 31 | 35 | 8 | 26 | 22*³ | ||
| Compression set 180℃ x 22 h | 20 | 13 | 22 | 9 | 10 | — | 17 | 14*4 | |||
| Dielectric breakdown strength kV | Normal state | — | — | — | — | 28 | 28 | — | — | 22 | |
| Submerged | — | — | — | — | 190 | 100 | 0.1 | — | 0.4 | ||
| Remarks | Middle fatigue durability | High fatigue durability | High decrement | Low motion magnification | Tracking property 3.5 kV | Tracking property 4.5 kV | High dielectricity | Specific resistance 0.2 Ω．M | — | ||
| Measurement: in accordance with JIS K 6249 Test pieces: 160°C x 10 min (press cure), 200°C x 4 h (post cure) | |||||||||||
| ✽1 Standard addition quantity is the quantity of the curing agent added to 100 parts compound | |||||||||||
| ✽2 Linear shrinkage calues differ according to the curing agent used | |||||||||||
| ✽3 Angle piece | |||||||||||
| ✽4 Me asured values at 150°C x 22 h | |||||||||||
| *A SHORE A. | |||||||||||
| [Unit conversion] tensile strength: 10 kgf/cm2 = 0.98 Mpa; tear strength: 1 kgf/cm = 0.98 kN/m; volume resistivity: 1014Ω•cm = 1TΩ•cm | |||||||||||
| Classification | For general extrusion molding, FDA, BfR | For tubing | |||||||||||||
| Grade | KE-541-U*³ | KE-551-U*³ | KE-561-U*³ | KE-571-U*³ | KE-581-U*³ | KE-153-U | KE-174-U | KE-1551-U*³ | KE-1571-U*³ | ||||||
| Appearance | Milky white translucent | Miky white translucent | |||||||||||||
| Density 23℃ g/cm³ | 1.10 | 1.14 | 1.17 | 1.22 | 1.24 | 1.16 | 1.21 | 1.16 | 1.19 | ||||||
| Williams plasticity (10 min after remix) | 150 | 200 | 250 | 360 | 430 | 260 | 370 | 270 | 320 | ||||||
| Curing agent | Curing agent name | C-23N | C-25A/B | C-23N | C-25A/B | C-23N | C-25A/B | C-23N | C-25A/B | C-23N | C-25A/B | C-25A/B | C-25A/B | C-23N | C-23N |
| Standard addition quantity*¹ | 1.0 | 0.5/2.0 | 1.0 | 0.5/2.0 | 1.0 | 0.5/2.0 | 1.0 | 0.5/2.0 | 1.0 | 0.5/2.0 | 0.5/2.0 | 0.5/2.0 | 0.8 | 0.7 | |
| Linear shrinkage*² % | — | — | — | — | — | — | — | 3.3 | — | ||||||
| Physical strength | Hardness Durometer A | 40 | 40 | 50 | 50 | 63 | 62 | 70 | 68 | 79 | 77 | 53 | 71 | 56 | 74 |
| Tensile strength MPa | 8.0 | 8.2 | 10.5 | 9.8 | 11.5 | 11.5 | 11.0 | 11.0 | 10.5 | 10.5 | 10.0 | 8.1 | 10.5 | 9.5 | |
| Elongation at break % | 550 | 690 | 530 | 590 | 450 | 470 | 430 | 450 | 310 | 430 | 650 | 520 | 530 | 370 | |
| Tear strength crescent piece kN/m | 10 | 22 | 13 | 26 | 15 | 24 | 19 | 26 | 13 | 23 | 36 | 37 | 16 | 23 | |
| Compression set 180℃ x 22 h | 12*4 | 9*5 | 8*4 | 9*5 | 11*4 | 9*5 | 13*4 | 9*5 | 14*4 | 9*5 | — | — | — | 35*5 | |
| Dielectric breakdown strength Normal state kV | — | — | 26 | — | 25 | — | 26 | — | 29 | — | 26 | 28 | 28 | 25 | |
| Volume resistivity Normal state TΩ．m | 30 | — | 70 | — | 300 | — | 500 | — | 700 | — | 900 | 650 | 600 | 600 | |
| Classification | High strength | Low hardness, high elongation | Flame retardance | |||||||||
| Grade | KE-555-U* | KE-131-U | KE-5620W-U | |||||||||
| Appearance | Pale yellow | Milky white translucent | White | Black | Charcoal | Charcoal | Translucent | |||||
| Density 23℃ g/cm³ | 1.17 | 1.21 | 1.07 | 1.06 | 1.13 | 1.13 | 1.40 | 1.38 | 1.49 | 1.42 | 1.20 | |
| 310 | 320 | 150 | 150 | 170 | 180 | 240 | 230 | 230 | 300 | 330 | ||
| Curing agent | Curing agent name | C-8 | C-8 | C-8 | C-8 | C-8A | C-15 | X-93-1609*6/C-3 | C-3 | C-3 | C-25A/B | |
| Standard addition quantity*¹ | 2.0 | 2.0 | 2.0 | 2.0 | 0.5 | 1.5 | 0.1/1.3 | 1.3 | 1.3 | 1.0/2.0 | ||
| Linear shrinkage*² % | 4.0 | 4.0 | 4.7 | 4.5 | 3.8 | 4.1 | 3.1 | 3.2 | 2.7 | 2.7 | 3.4 | |
| Physical strength | Hardness Durometer A | 53 | 70 | 18 | 23 | 35 | 39 | 59 | 57 | 60 | 57 | 70 |
| Tensile strength MPa | 11.0 | 9.4 | 7.4 | 5.0 | 9.7 | 9.7 | 6.5 | 7.0 | 7.2 | 7.3 | 7.7 | |
| Elongation at break % | 650 | 550 | 1,060 | 770 | 880 | 700 | 410 | 430 | 290 | 320 | 370 | |
| Tear strength crescent piece kN/m | 35 | 41 | 18 | 10 | 34 | 17 | 12 | 11 | 13 | 10 | 14 | |
| Compression set 180℃ x 22 h | 31 | 18 | — | 22 | 20*5 | 9*5 | 21 | 27 | 16 | 22 | 20 | |
| Dielectric breakdown strength Normal state kV | 27 | 27 | — | — | — | — | 27 | 28 | 27 | 29 | 19 | |
| Volume resistivity Normal state TΩ．m | 100 | 200 | — | — | — | — | 50 | 80 | 240 | 8 | 300 | |
| Flame retardance UL94*7 | — | — | — | — | — | — | V-0 | V-0 | V-0 | V-0 | V-1 | |
| Measurement: in accordance with JIS K 6249 Test pieces: 165°C x 10 min (press cure), 200°C x 4 h (post cure) | ||||||||||||
| ✽1 Standard addition quantity is the quantity of the curing agent added to 100 parts compound | ||||||||||||
| ✽2 Linear shrinkage calues differ according to the curing agent used | ||||||||||||
| ✽3 Test pieces: 120°C x 10 min (press cure), 200°C 4 h (post cure) | ||||||||||||
| ✽4 Measured values at 100°C x 22 h | ||||||||||||
| ✽5 Measured values at 150°C x 22 h | ||||||||||||
| ✽6 X-93-1609 is a flame retardant | ||||||||||||
| ✽7 UL File No.E48923 | ||||||||||||
| ✽A SHORE A | ||||||||||||
| ⋆ Not available in U.S.. | ||||||||||||
| [Unit conversion] tensile strength: 10 kgf/cm2 = 0.98 Mpa; tear strength: 1 kgf/cm = 0.98 kN/m; volume resistivity: 1014Ω•cm = 1TΩ•cm | ||||||||||||
成型通用
描述
KCC通用擠出矽橡膠產品是肖氏A硬度的化合物
30, 40, 50, 60,70 和 80。它們旨在促進與增量填料和添加劑的混合。
除了機械和電氣性能外，這些產品還具有出色的加工能力和
透明度。此外，通過混合每個等級可以製成各種硬度等級。橡膠件是
通常採用擠出工藝製成，也可以採用壓縮成型方法。
特徵
- 良好平衡的機械性能
- 在擠出和成型等方面具有出色的加工能力
- 良好的回彈性
- 通過 UL 94 HB 測試
- 符合 FDA 和 BfR 對食品接觸物品的建議
應用
- 一般工業用品（密封件、型材、片材、墊圈）
- 食品接觸用品（管道、管材、廚具、包裝）
- 電氣用品
| Properties | Test method | Unit | SH0030U | SH0040U | SH0050U | SH0060U | SH0070U | SH0080U |
|---|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Translucent | Light grey | ||||
| Williams plasticity | ASTM D926 | — | 130 | 160 | 180 | 210 | 240 | 290 |
| Specific gravity | ASTM D792 | — | 1.10 | 1.13 | 1.15 | 1.23 | 1.30 | 1.44 |
| Hardness | ASTM D2240 | Shore A | 30 | 40 | 50 | 60 | 70 | 80 |
| Tensile strength | ASTM D412 | Mpa | 7.5 | 8.5 | 9.0 | 8.0 | 7.9 | 7.0 |
| Elongation | ASTM D412 | % | 850 | 700 | 500 | 250 | 180 | 120 |
| Tear strength | ASTM D624 C | N/mm | 20 | 24 | 20 | 22 | 20 | 16 |
| Resilience | ASTM D1054 | % | 58 | 63 | 63 | 52 | 49 | 44 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 20 | 18 | 18 | 14 | 14 | 25 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | ||||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||||||
| Properties | Test method | Unit | SH5060U | SH5070U | SH5180U | SH5360U | SH5960U |
|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Translucent | ||||
| Williams plasticity | ASTM D926 | — | 210 | 250 | 300 | 220 | 210 |
| Specific gravity | ASTM D792 | — | 1.18 | 1.20 | 1.22 | 1.18 | 1.18 |
| Hardness | ASTM D2240 | Shore A | 60 | 70 | 80 | 60 | 60 |
| Tensile strength | ASTM D412 | Mpa | 8.5 | 7.7 | 7.0 | 8.5 | 8.5 |
| Elongation | ASTM D412 | % | 400 | 230 | 190 | 350 | 400 |
| Tear strength | ASTM D624 C | N/mm | 22 | 24 | 24 | 25 | 26 |
| Resilience | ASTM D1054 | % | 58 | 57 | 50 | 59 | 62 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 16 | 17 | 15 | 16 | 19 |
| Properties | Test method | Unit | SH830U | SH840U | SH850U | SH5860U |
|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Translucent | |||
| Williams plasticity | ASTM D926 | — | 130 | 160 | 190 | 210 |
| Specific gravity | ASTM D792 | — | 1.10 | 1.13 | 1.16 | 1.17 |
| Hardness | ASTM D2240 | Shore A | 30 | 40 | 50 | 60 |
| Tensile strength | ASTM D412 | Mpa | 8.3 | 7.3 | 7.5 | 7.6 |
| Elongation | ASTM D412 | % | 680 | 550 | 360 | 210 |
| Tear strength | ASTM D624 C | N/mm | 18 | 20 | 22 | 19 |
| Resilience | ASTM D1054 | % | 56 | 61 | 62 | 70 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 25 | 19 | 18 | 12 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | ||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||||
擠出通用
描述
KCC通用擠出矽橡膠產品是肖氏A硬度的化合物30, 40, 50, 60,70 和 80。它們旨在促進與增量填料和添加劑的混合。除了機械和電氣性能外，這些產品還具有出色的加工能力和透明度。此外，通過混合每個等級可以製成各種硬度等級。橡膠件是通常採用擠出工藝製成，也可以採用壓縮成型方法。特徵
優異的機械和電氣性能
- 在擠出和成型等方面具有出色的加工能力
- 良好的透明度
- 使用 SH0008B 添加劑穩定時具有良好的耐熱性
- 符合 FDA 和 BfR 對食品接觸物品的建議
應用
- 一般工業用品（密封件、型材、片材、墊圈）
- 食品接觸用品（管道、管材、廚具、包裝）
- 電氣用品
| Properties | Test method | Unit | SH1021U | SH1032U | SH1040U | SH1041U | SH1050U |
|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Transparent | ||||
| Williams plasticity | ASTM D926 | — | 150 | 150 | 150 | 160 | 180 |
| Specific gravity | ASTM D792 | — | 1.09 | 1.10 | 1.11 | 1.12 | 1.13 |
| Hardness | ASTM D2240 | Shore A | 33 | 38 | 42 | 45 | 52 |
| Tensile strength | ASTM D412 | Mpa | 7.0 | 6.8 | 7.0 | 8.0 | 8.5 |
| Elongation | ASTM D412 | % | 610 | 550 | 500 | 550 | 450 |
| Tear strength | ASTM D624 C | N/mm | 15 | 20 | 20 | 23 | 24 |
| Resilience | ASTM D1054 | % | 13 | 10 | 10 | 14 | 13 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 85 | 55 | 60 | 60 | 43 |
| Volume resistivity | ASTM D257 | Ω．cm | 1.6X10(16) | 1.7X10(16) | 1.7X10(16) | 2.7X10(16) | 2.1X10(15) |
| Dielectric strength | ASTM D149 | kV/mm | 24 | 25 | 23 | 22 | 22 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | |||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||||
| Properties | Test method | Unit | SH1060U | SH1061U | SH1070U | SH1072U | SH1073U | SH1080U |
|---|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Transparent | |||||
| Williams plasticity | ASTM D926 | — | 220 | 210 | 275 | 270 | 270 | 300 |
| Specific gravity | ASTM D792 | — | 1.16 | 1.16 | 1.19 | 1.18 | 1.19 | 1.2 |
| Hardness | ASTM D2240 | Shore A | 62 | 62 | 72 | 72 | 72 | 82 |
| Tensile strength | ASTM D412 | Mpa | 9.5 | 9.5 | 9.5 | 10.0 | 9.5 | 9.0 |
| Elongation | ASTM D412 | % | 350 | 250 | 300 | 300 | 420 | 160 |
| Tear strength | ASTM D624 C | N/mm | 25 | 27 | 25 | 29 | 28 | 25 |
| Resilience | ASTM D1054 | % | 15 | 15 | 18 | 15 | 25 | 10 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 35 | 35 | 45 | 33 | 60 | 30 |
| Volume resistivity | ASTM D257 | Ω．cm | 1.6X10(15) | 44X10(16) | 3.8X10(15) | 4.0X10(16) | 1.0X10(15) | 7.1X10(14) |
| Dielectric strength | ASTM D149 | kV/mm | 27 | 28 | 26 | 27 | 28 | 22 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | ||||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||||||
低硬度 HTV
描述
這些產品在固化狀態下具有低硬度（肖氏 A 硬度 9 ~ 20）。 可用於需要柔軟手感的運動用品、醫療用品等矽橡膠製品
特徵
- 低邵氏 A 硬度和高彈性伸長率
- 出色的成型和注塑加工能力
- 符合 FDA 和 BfR 對食品接觸製品的建議
應用
- 游泳用品（泳帽、護目鏡帶）
- 嬰兒護理用品（玩具、蓋子）
- 高彈性製品（條帶、膠帶）
| Properties | Test method | Unit | SH0005U | SH1020U | SH0010U | SH0020U |
|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Transparent | Translucent | ||
| Williams plasticity | ASTM D926 | — | 125 | 105 | 90 | 100 |
| Specific gravity | ASTM D792 | — | 1.03 | 1.08 | 1.06 | 1.08 |
| Hardness | ASTM D2240 | Shore A | 9 | 23 | 10 | 22 |
| Tensile strength | ASTM D412 | Mpa | 2.3 | 4.0 | 4.0 | 5.5 |
| Elongation | ASTM D412 | % | 950 | 970 | 950 | 1,000 |
| Tear strength | ASTM D624 C | N/mm | 7 | 15 | 9 | 13 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 55 | 65 | 26 | 18 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | ||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||||
高硬度 HTV
描述
該系列由固化狀態下硬度為 90（鞋 A）的高硬度矽橡膠化合物組成。 這些較硬的牌號可以用來調整其他牌號的硬度，它們也有自己的應用
特徵
- 超高邵氏 A 硬度 90
- 高威廉斯可塑性和高生坯強度
- 符合 FDA 和 BfR 對食品接觸物品的建議
應用
- 一般工業用品（鍵盤的鍵頂、特殊滾輪）
- Fiid 接觸用品（廚具、瓶子）
| Properties | Test method | Unit | SH5190U | SH1090U |
|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Translucent | Transparent |
| Williams plasticity | ASTM D926 | — | 300 | 340 |
| Specific gravity | ASTM D792 | — | 1.25 | 1.23 |
| Hardness | ASTM D2240 | Shore A | 90 | 90 |
| Tensile strength | ASTM D412 | Mpa | 8.5 | 9.5 |
| Elongation | ASTM D412 | % | 50 | 150 |
| Tear strength | ASTM D624 C | N/mm | 16 | 24 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 20 | 19 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | ||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||
高撕裂強度 HTV
描述
這些產品具有優異的機械性能，包括高撕裂強度，它們用於形狀複雜的零件、大型成型零件等應用。SH7340U和SH7255U本身俱有良好的熱穩定性，SH7060U和SH7070U與添加劑SH0008B具有良好的熱穩定性。
特徵
- 高撕裂強度和高拉伸強度
- 在成型和擠出等方面具有出色的加工能力
- 良好的耐熱性（SH7340U 和 SH7255U）
- 符合 FDA 和 BfR 對食品接觸物品的建議（SH7060U 和 SH7070U）
應用
- 一般工業零件（橡膠標籤紡織品、旋鑄、片材、墊圈）
- 高機械橡膠製品
- 汽車製品（消聲器衣架）
| Properties | Test method | Unit | SH7340U | SH7255U | SH7060U | SH7070U |
|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Transparent | |||
| Williams plasticity | ASTM D926 | — | 150 | 215 | 200 | 240 |
| Specific gravity | ASTM D792 | — | 1.12 | 1.16 | 1.16 | 1.18 |
| Hardness | ASTM D2240 | Shore A | 40 | 60 | 60 | 70 |
| Tensile strength | ASTM D412 | Mpa | 8.3 | 10.3 | 9.5 | 9.0 |
| Elongation | ASTM D412 | % | 980 | 850 | 800 | 700 |
| Tear strength | ASTM D624 C | N/mm | 45 | 45 | 40 | 42 |
| Resilience | ASTM D1054 | % | 37 | 39 | 36 | 39 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 24 | 29 | 26 | 28 |
| Property change after heat aging 72 hours at 220℃ | ||||||
| Hardness | ASTM D573 | — | -2 | 2 | 6 | 5 |
| Tensile strength | % | -28 | -19 | -33 | -28 | |
| Elongation | % | -25 | -23 | -38 | -36 | |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | ||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||||
低壓縮永久變形 HTV
描述
這些產品旨在具有出色的壓縮永久變形，無需後固化。
特徵
- 低壓縮永久變形，無需後固化。
應用
- 一般工業用品
（OA 輥、填料、墊圈、片材、密封件、O 形圈）
| Properties | Test method | Unit | SH2533U | SH2540U | SH2580U |
|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Translucent | Light yellow | Beige |
| Williams plasticity | ASTM D926 | — | 110 | 140 | 250 |
| Specific gravity | ASTM D792 | — | 1.04 | 1.10 | 1.43 |
| Hardness | ASTM D2240 | Shore A | 33 | 40 | 80 |
| Tensile strength | ASTM D412 | Mpa | 1.8 | 7.0 | 7.5 |
| Elongation | ASTM D412 | % | 260 | 550 | 100 |
| Tear strength | ASTM D624 C | N/mm | 9 | 23 | 18 |
| Resilience | ASTM D1054 | % | 85 | 67 | 53 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 7 | 13 | 10 |
| Property change after heat aging 72 hours at 220℃ | |||||
| Hardness | ASTM D573 | — | -10 | -5 | 5 |
| Tensile strength | % | -32 | -20 | -30 | |
| Elongation | % | 5 | 5 | -50 | |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 1.0 phr | |||||
| ※ Curing condition : | |||||
| - SH2533U : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||
| - SH2540U, SH2580U : 10mins t 170℃ press cure | |||||
耐蒸汽 HTV
描述
這些產品用於需要耐蒸汽、耐熱和耐油以及在高溫下具有優異機械性能的各種零件。
肖氏 A 硬度範圍為 50 至 70。
特徵
- 耐蒸汽和耐熱性能
- 低壓縮永久變形
- 出色的加工能力
應用
- 包裝（蒸汽電飯鍋、蒸汽熨斗、罐子、高壓釜等）
- 其他工業用品（O 形圈、墊圈、閥門）
| Properties | Test method | Unit | SH6050U | SH6060U | SH6070U |
|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Light yellow | ||
| Williams plasticity | ASTM D926 | — | 170 | 220 | 210 |
| Specific gravity | ASTM D792 | — | 1.13 | 1.15 | 1.17 |
| Hardness | ASTM D2240 | Shore A | 50 | 60 | 70 |
| Tensile strength | ASTM D412 | Mpa | 8 | 9.0 | 7.0 |
| Elongation | ASTM D412 | % | 500 | 530 | 120 |
| Tear strength | ASTM D624 C | N/mm | 23 | 27 | 20 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 10 | 13 | 6 |
| Property change after heat aging 72 hours at 220℃ | |||||
| Hardness | ASTM D573 | — | 1 | 1 | -1 |
| Tensile strength | % | -7 | -24 | -33 | |
| Elongation | % | -29 | -35 | -23 | |
| Property change after heat aging 168 hours at 3 bars, 130℃ | |||||
| Hardness | ASTM D471 | — | 2 | 4 | -1 |
| Tensile strength | % | -2 | -2 | -8 | |
| Elongation | % | -13 | -14 | -1 | |
| Volume | % | -1 | -1 | -1 | |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | |||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||
導電 HTV
描述
導電系列是熱固化化合物，用於壓製成型、擠出和日曆。肖氏 A 硬度範圍為 60 至 80。
特徵
- 耐蒸汽和耐熱性能
- 低壓縮永久變形
- 出色的加工能力
應用
- 包裝（蒸汽電飯鍋、蒸汽熨斗、罐子、高壓釜等）
- 其他工業用品（O 形圈、墊圈、閥門）
| Properties | Test method | Unit | SH6540U | SH6560U | SH6570U | SH6580U |
|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Black | |||
| Williams plasticity | ASTM D926 | — | 200 | 580 | 730 | 800 |
| Specific gravity | ASTM D792 | — | 1.08 | 1.17 | 1.19 | 1.21 |
| Hardness | ASTM D2240 | Shore A | 36 | 60 | 70 | 80 |
| Tensile strength | ASTM D412 | Mpa | 4.5 | 6.7 | 6.5 | 7.0 |
| Elongation | ASTM D412 | % | 700 | 380 | 180 | 90 |
| Tear strength | ASTM D624 C | N/mm | 15 | 21 | 15 | 14 |
| Volume resistivity | ASTM D991 | Ω.cm | 45 | 9.0 | 5.0 | 3.0 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 2.0 phr | ||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | ||||||
導熱 HTV
描述
固化產品具有阻燃性 (UL 94 V-0) 和導熱性 (~ 1.0 W/mK)。因此，它被用於電子設備以從設備中去除熱量。
特徵
- 高導熱性
- 高耐熱性和阻燃性
- 優異的成型和擠出等加工能力
應用
- 用於電子設備的導熱製品（散熱墊、片、蓋）
| Properties | Test method | Unit | SH6280U |
|---|---|---|---|
| Appearance | ASTM E1767 | — | Dark grey |
| Williams plasticity | ASTM D926 | — | 290 |
| Specific gravity | ASTM D792 | — | 2.17 |
| Hardness | ASTM D2240 | Shore A | 80 |
| Tensile strength | ASTM D412 | Mpa | 4.0 |
| Elongation | ASTM D412 | % | 85 |
| Tear strength | ASTM D624 C | N/mm | 9 |
| Volume resistivity | ASTM D257 | Ω.cm | 3.0X10(14) |
| Dielectric strength | ASTM D149 | KV/mm | 26 |
| Thermal conductivity | ASTM D5470 | W/m.k | 1.0 |
| Property change after heat aging 72 hours at 250℃ | |||
| Hardness | ASTM D573 | — | 1 |
| Tensile strength | % | -10 | |
| Elongation | % | -13 | |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 2.0 phr | |||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||
阻燃 HTV
描述
這些產品分別是阻燃等級 (UL 94 V-0)。（UL 文件編號：QMFZ8.E253047）
特徵
- 阻燃等級（UL 94 V-0）
- 在成型和擠出等方面具有出色的加工能力
- 良好的機械和電氣性能
應用
- 電子產品（高壓帽、背光燈座、特殊寬幅）
- 建築用品（防火墊圈）
| Properties | Test method | Unit | SH1520U | SH1550U | SH1572U |
|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Dark grey | White | |
| Williams plasticity | ASTM D926 | — | 200 | 200 | 220 |
| Specific gravity | ASTM D792 | — | 1.44 | 1.42 | 1.48 |
| Hardness | ASTM D2240 | Shore A | 60 | 55 | 70 |
| Tensile strength | ASTM D412 | Mpa | 7.8 | 8.7 | 6.3 |
| Elongation | ASTM D412 | % | 320 | 450 | 160 |
| Tear strength | ASTM D624 C | N/mm | 23 | 23 | 16 |
| Volume resistivity | ASTM D257 | Ω.cm | 9.0X10(15) | 3.0X10(16) | 3.4X10(15) |
| Dielectric strength | ASTM D149 | KV/mm | 24 | 26 | 24 |
| Flame retardancy | UL 94 | — | V-0 | V-0 | V-0 |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 2.0 phr | |||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||
電線電纜 HTV
描述
這些產品是電線電纜擠出級，肖氏硬度為 60 和 70。它們具有優異的擠出性能。
特徵
- 優異的溫度穩定性
- 優異的擠出加工能力
- 良好的機械和電氣性能
應用
- 電線和電纜（通用/熱穩定/高介電設備）
- 玻璃和陶瓷包裝
| Properties | Test method | Unit | SH1160U | SH1170U | SH1270U | SH1775U | SH1370U |
|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | White | Belge | White | Light grey | Light yellow |
| Williams plasticity | ASTM D926 | — | 200 | 200 | 230 | 210 | 240 |
| Specific gravity | ASTM D792 | — | 1.40 | 1.40 | 1.33 | 1.29 | 1.20 |
| Hardness | ASTM D2240 | Shore A | 60 | 70 | 70 | 65 | 70 |
| Tensile strength | ASTM D412 | Mpa | 7.5 | 7.5 | 8.0 | 7.5 | 9.0 |
| Elongation | ASTM D412 | % | 330 | 200 | 250 | 200 | 260 |
| Tear strength | ASTM D624 C | N/mm | 23 | 18 | 24 | 17 | 23 |
| Volume resistivity | ASTM D257 | Ω.cm | 2.0X10(15) | 1.0X10(15) | 1.3X10(16) | 8.5X10(14) | 1.5X10(16) |
| Dielectric strength | ASTM D149 | KV/mm | 27 | 28 | 30 | 24 | 30 |
| Property change after heat aging as below condition | |||||||
| Hardness change | ASTM D573 | — | 1 | 1 | 7 | -3 | 2 |
| Tensile strength | ASTM D573 | — | 1 | 1 | 7 | -3 | 2 |
| Elongation change | % | -13 | -15 | -30 | -31 | -30 | |
| Elongation | % | -7 | -6 | -45 | -38 | -40 | |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 2.0 phr | |||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||||
高壓絕緣子用HTV
描述
該產品是一種用於高膠粘劑絕緣應用的模塑料。它已經與過氧化物催化劑混合使用。
特徵
- 出色的耐電痕性和耐腐蝕性
- 出色的耐候性和抗紫外線性
- 出色的電絕緣性能
- 出色的防水性
- 出色的注塑成型加工能力
應用
- 高壓絕緣子、電纜終端和連接器
- 避雷器、懸式絕緣子
| Properties | Test method | Unit | SH4001Z | SH4001ZNC133 |
|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Dark grey | Grey |
| Williams plasticity | ASTM D926 | — | 200 | 200 |
| Specific gravity | ASTM D792 | — | 1.55 | 1.55 |
| Hardness | ASTM D2240 | Shore A | 65 | 65 |
| Tensile strength | ASTM D412 | Mpa | 3.8 | 3.8 |
| Elongation | ASTM D412 | % | 220 | 280 |
| Tear strength | ASTM D624 C | N/mm | 16 | 15 |
| Volume resistivity | ASTM D257 | Ω.cm | 2.3X10(13) | 2.2X10(13) |
| Dielectric strength | ASTM D149 | KV/mm | 26 | 26 |
| Dielectric constant at 1 MHz | ASTM D150 | — | 3.8 | 3.8 |
| Dissipation factor at 1MHz | ASTM D150 | — | 0.01 | 0.01 |
| Tracking resistance | IEC 60587 | kV | 4.5 | 4.5 |
| ※ They are already mixed curing agent | ||||
| : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 1.0 phr | ||||
| ※ Curing condition : 10mins at 170℃ press cure | ||||
放油 HTV
描述
這些產品在固化後向表面彈性體製品釋放潤滑油。這允許容易的組裝和防水性能。它們可以通過各種加工方法使用，例如注塑、傳遞模塑和壓延。
特徵
- 良好的耐熱性和耐油性
- 優異的注塑、傳遞成型加工能力
- 良好的機械性能
應用
- 汽車用品（線束連接器、索環、單線墊圈、平墊圈）
- 工業用品（O 形圈、油封）
| Properties | Test method | Unit | SH9030U | SH9035U | SH9040U | SH9050U | SH9060U |
|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Milky White | Beige | |||
| Williams plasticity | ASTM D926 | — | 150 | 175 | 175 | 170 | 210 |
| Specific gravity | ASTM D792 | — | 1.13 | 1.15 | 1.15 | 1.16 | 1.22 |
| Hardness | ASTM D2240 | Shore A | 30 | 32 | 40 | 50 | 60 |
| Tensile strength | ASTM D412 | Mpa | 8.5 | 9.5 | 8.5 | 8.5 | 8.0 |
| Elongation | ASTM D412 | % | 510 | 630 | 440 | 400 | 330 |
| Tear strength | ASTM D624 C | N/mm | 19 | 21 | 22 | 23 | 22 |
| Compression set 22hrs at 175℃ | ASTM D395 | W/m.k | 24 | 25 | 26 | 13 | 10.0 |
| Property change after heat aging 72 hours at 220℃ | |||||||
| Hardness | ASTM D573 | — | -2 | -3 | -1 | 2 | 5 |
| Tensile strength | % | -5 | -20 | -14 | -7 | -12 | |
| Elongation | % | -7 | -20 | -13 | -15 | -24 | |
| Property change after IRM 903 oil aging 72 hours at 150℃ | |||||||
| Hardness | ASTM D471 | — | -19 | -14 | -20 | -16 | -24 |
| Tensile strength | % | -47 | -38 | -40 | -37 | -24 | |
| Elongation | % | -20 | -16 | -15 | -30 | -13 | |
| Volume | % | 50 | 38 | 45 | 36 | 35 | |
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | |||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||||
高抗疲勞 HTV
描述
這些產品專為高動態物品（鍵盤、單鍵球機）而設計
特徵
- 優異的動態耐久性
- 高回彈彈性
- 卓越的成型加工能力
- 高分散性
- 低壓縮永久變形
應用
- 電子產品（動態小鍵盤、鍵盤按鍵開關）
- 各種工業用途，具有高耐用性
| Properties | Test method | Unit | SH9141U | SH9151U | SH9161U | SH918U | SH9182U |
|---|---|---|---|---|---|---|---|
| Appearance | ASTM E1767 | — | Transparent | ||||
| Williams plasticity | ASTM D926 | — | 150 | 180 | 160 | 300 | 270 |
| Specific gravity | ASTM D792 | — | 1.08 | 1.11 | 1.11 | 1.19 | 1.18 |
| Hardness | ASTM D2240 | Shore A | 40 | 50 | 60 | 80 | 83 |
| Tensile strength | ASTM D412 | Mpa | 7.0 | 8.5 | 8.0 | 9.5 | 9.5 |
| Elongation | ASTM D412 | % | 470 | 420 | 250 | 200 | 200 |
| Tear strength | ASTM D624 C | N/mm | 25 | 30 | 25 | 20 | 23 |
| Resilience | ASTM D1054 | % | 80 | 78 | 75 | 60 | 63 |
| Compression set 22hrs at 175℃ | ASTM D395 | % | 12 | 11 | 12 | 13 | 13 |
| Fatigue resistant degree | ASTM D4482 | cycle | 6,000,000 | 1,500,000 | 1,650,000 | 500,000 | 1,000,000 |
| For SH9141U, SH9151U and SH9161U | |||||||
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | |||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||||
| ※ Fatigue resistant test condition : 150% elongation 5 cycle/sec | |||||||
| For SH9181U and SH9182U | |||||||
| ※ Curing agent : KC-8 (2,5-dimethyl 2,5-di(t-butyl peroxy) hexane 45% paste) 0.5 phr | |||||||
| ※ Curing condition : 10mins at 170℃ press cure → 4 hours at 200 ℃ hot air. | |||||||
| ※ Fatigue resistant test condition : 150% elongation 5 cycle/sec | |||||||